Anti-skid Geomembrane
Anti-skid Geomembrane is made of waterproof materials with basic raw material of high molecular polymer.
Thickness:0.1-2.5mm
Anti-skid Geomembrane is made of waterproof materials with basic raw material of high molecular polymer.
Thickness:0.1-2.5mm
It is applied in landfill waste site sewage and silth treatmentsite.tailing depot and underground construction project.
· Quality inspection standard: GB/T176431998
· Quality control measure: strictly complies with ISO9001:2000
· Technical specifications of HDPE geo-membrane:
o Density: ≥0.94g/m2
o Tensile strength: ≥17MPa
o Elongation at break: ≥500%
o Right-angled tear: ≥80N/mm
o CBR Mullen burst: ≥3.0kN
o Puncture strength: ≥ 550N
o -70 low temperature impact brittle property: very good
o Chemical Resistance at 80, marinated in 5g/L NaCl for a long time, it will not erode or swell
Point anti-skid geo-membrane is a new type of anti-leakage products, its one side point anti-skid and both sides point anti-skid can increase its coefficient of friction and function of preventing leakage, especially used in anti-leakage in slope and vertical surface in order to enhance its stability
Technical data of textured HDPE geomembrane
Property | Test method | |||||||||||||
1.0mm | 1.25mm | 1.5mm | 2.0mm | 2.5mm | 3.0mm | |||||||||
Height of textured (mm) | 0.25 | |||||||||||||
Density (≥g/cm³) | 0.939 | |||||||||||||
Yield strength (N/mm) | 15 | 18 | 22 | 29 | 37 | 44 | ||||||||
Breaking strength(N/mm) | 10 | 13 | 16 | 21 | 26 | 32 | ||||||||
Yield Elongation (%) | 12 | |||||||||||||
Breaking Elongation(%) | 100 | |||||||||||||
Right angle Tear strength (N) | 125 | 156 | 187 | 249 | 311 | 374 | ||||||||
Puncture Strength (n) | 267 | 333 | 400 | 534 | 667 | 800 | ||||||||
Anti-environmental cracking (/hr) | 300 | |||||||||||||
Black carbon content (%) | 2.0-3.0 | |||||||||||||
85 celsius oven aging ( min average data) | Standard % | 55 | ||||||||||||
High pressure % | 80 | |||||||||||||
UV Resistance (%) | 50 | |||||||||||||
-70 celsius performance of low-temperature | Pass | |||||||||||||
Water vapor permeability coeffcient (g·cm/sq.cm·s·Pa) | ≤1.0x10-10 | |||||||||||||
Dimensional stability (%) | +/-2 | |||||||||||||
OIT OIT/min | Standard | 100 | ||||||||||||
High pressure | 400 |